HOME > Article > DetailCrystallographic orientation dependence of deformation-induced martensitic transformation of 1.3 GPa-class 0.6 %C bainitic steel with retained austeniteRintaro Ueji, Akinobu Shibata, Kohsaku Ushioda, Yuuji Kimura, Takahito Ohmura, Tadanobu Inoue. Scripta Materialia 194 113666. 2021.https://doi.org/10.1016/j.scriptamat.2020.113666 NIMS author(s)UEJI, RintaroSHIBATA, AkinobuKIMURA, YuujiOHMURA, TakahitoINOUE, TadanobuFulltext and dataset(s) on Materials Data Repository (MDR)Created at :2020-12-21 03:00:18 +0900 Updated at :2021-09-28 22:27:07 +0900